- 彎曲模量 [MPa]: 12.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.68 g/cc | 1.68 g/cc | ISO 1183 | ||
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h | ||
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 180 MPa | 26100 psi | |||
| Elongation at Yield | 2.0 % | 2.0 % | |||
| 2.3 % | 2.3 % | flexural | |||
| Modulus of Elasticity | 14.0 GPa | 2030 ksi | |||
| Flexural Strength | 260 MPa | 37700 psi | |||
| Flexural Modulus | 12.0 GPa | 1740 ksi | |||
| Charpy Impact Unnotched | 4.50 J/cm2 | 21.4 ft-lb/in2 | edgewise; ISO 179 1eU | ||
| 5.10 J/cm2 @Temperature -30.0 °C | 24.3 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 250 °C | 482 °F | |||
| 280 °C | 536 °F | short term | |||
| Vicat Softening Point | 325 °C | 617 °F | DIN ISO 306 | ||
| Flammability, UL94 | V-0 | V-0 | not recognized by UL | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 390 °C | 734 °F | mass temp | ||
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |||
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |||
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |||
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |||
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |||
| Drying Temperature | 120 °C @Time 21600 - 28800 sec | 248 °F @Time 6.00 - 8.00 hour | or | ||
| 150 °C @Time 10800 - 21600 sec | 302 °F @Time 3.00 - 6.00 hour | Dehumidifying dryer | |||
| Descriptive Properties | |||||
| Color | natural color | ||||