- 彎曲模量 [MPa]: 24.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ISO 1183 | ||
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h | ||
| Linear Mold Shrinkage | 0.00050 - 0.0020 cm/cm | 0.00050 - 0.0020 in/in | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 265 MPa | 38400 psi | |||
| Elongation at Yield | 1.6 % | 1.6 % | |||
| 2.0 % | 2.0 % | flexural | |||
| Modulus of Elasticity | 28.0 GPa | 4060 ksi | |||
| Flexural Strength | 380 MPa | 55100 psi | |||
| Flexural Modulus | 24.0 GPa | 3480 ksi | |||
| Charpy Impact Unnotched | 5.50 J/cm2 | 26.2 ft-lb/in2 | edgewise; ISO 179 1eU | ||
| Charpy Impact, Notched | 0.800 J/cm2 | 3.81 ft-lb/in2 | ISO 179 1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | |||
| Insulation Resistance | <= 100000 ohm | <= 100000 ohm | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 250 °C | 482 °F | |||
| 280 °C | 536 °F | short term | |||
| Vicat Softening Point | 325 °C | 617 °F | DIN ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 390 °C | 734 °F | mass temp | ||
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |||
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |||
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |||
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |||
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |||
| Drying Temperature | 120 °C @Time 21600 - 28800 sec | 248 °F @Time 6.00 - 8.00 hour | or | ||
| 150 °C @Time 10800 - 21600 sec | 302 °F @Time 3.00 - 6.00 hour | Dehumidifying dryer | |||
| Descriptive Properties | |||||
| Color | natural color (black) | ||||