- 熔體流動(dòng)速率 [g/10min]: 32.64
- 彎曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ISO 1183 | ||
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h | ||
| Linear Mold Shrinkage | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | |||
| Melt Flow | 32.64 g/10 min @Load 10.0 kg, Temperature 380 °C | 32.64 g/10 min @Load 22.0 lb, Temperature 716 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 200 MPa | 29000 psi | |||
| Elongation at Yield | 2.3 % | 2.3 % | |||
| 2.6 % | 2.6 % | flexural | |||
| Modulus of Elasticity | 13.0 GPa | 1890 ksi | |||
| Flexural Strength | 295 MPa | 42800 psi | |||
| Flexural Modulus | 11.0 GPa | 1600 ksi | |||
| Charpy Impact Unnotched | 4.80 J/cm2 | 22.8 ft-lb/in2 | edgewise; ISO 179 1eU | ||
| Charpy Impact, Notched | 0.600 J/cm2 | 2.86 ft-lb/in2 | ISO 179 1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistance | <= 1.00e+7 ohm | <= 1.00e+7 ohm | |||
| Insulation Resistance | <= 1.00e+7 ohm | <= 1.00e+7 ohm | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 250 °C | 482 °F | |||
| 280 °C | 536 °F | short term | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 390 °C | 734 °F | mass temp | ||
| Nozzle Temperature | 360 - 380 °C | 680 - 716 °F | |||
| Zone 1 | 360 - 370 °C | 680 - 698 °F | |||
| Zone 2 | 380 - 390 °C | 716 - 734 °F | |||
| Zone 3 | 390 - 400 °C | 734 - 752 °F | |||
| Mold Temperature | 170 - 200 °C | 338 - 392 °F | |||
| Drying Temperature | 120 °C @Time 21600 - 28800 sec | 248 °F @Time 6.00 - 8.00 hour | or | ||
| 150 °C @Time 10800 - 21600 sec | 302 °F @Time 3.00 - 6.00 hour | Dehumidifying dryer | |||
| Descriptive Properties | |||||
| Color | black | ||||