- 密度 [g/cm3]: 1.44
- 缺口沖擊強度: 0.57
- 彎曲強度 [MPa]: 120.0
- 彎曲模量 [MPa]: 8.80
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | LATI | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | LATI | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 120 MPa | 17400 psi | ISO 527 | ||
| Flexural Modulus | 8.80 GPa | 1280 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.570 J/cm @Temperature 23.0 °C | 1.07 ft-lb/in @Temperature 73.4 °F | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ASTM D648 | ||
| Flammability, UL94 | V-0 @Thickness 0.750 mm | V-0 @Thickness 0.0295 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 365 - 385 °C | 689 - 725 °F | |||
| Mold Temperature | 180 - 190 °C | 356 - 374 °F | |||
| Drying Temperature | 150 - 170 °C | 302 - 338 °F | Always recommended, temperature can be reduced when using vacuum ovens. | ||
| Dry Time | >= 3 hour | >= 3 hour | Always recommended, drying time can be reduced when using vacuum ovens. | ||
| Descriptive Properties | |||||
| Injection Speed | medium | ||||