- 吸水率 [%]: 0.15
- 缺口沖擊強度: 0.854
- 拉伸強度 [MPa]: 145.0
- 彎曲模量 [MPa]: 7.58
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 | ||
| Water Absorption | 0.15 % | 0.15 % | 24 hr. Immersion, -; ASTM D570 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 102 | 102 | ASTM D785 | ||
| Tensile Strength, Yield | 145 MPa | 21000 psi | Type 1 - Rigids, Break, 0.2 in/min; ASTM D638 | ||
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Tensile Modulus | 8.27 GPa | 1200 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Flexural Strength | 221 MPa | 32000 psi | ASTM D790 | ||
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.854 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 1.60 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 0.0000239 μm/m-°C @Temperature 20.0 °C | 0.0000133 μin/in-°F @Temperature 68.0 °F | ASTM D696 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 285 °C | 545 °F | Annealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 382 - 393 °C | 720 - 740 °F | Molding | ||
| Mold Temperature | 149 °C | 300 °F | |||
| Drying Temperature | 149 °C | 300 °F | 2 hrs | ||
| Descriptive Properties | |||||
| Product Form | Pellets | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.