- 密度 [g/cm3]: 1.33
- 缺口沖擊強度: 0.571
- 彎曲模量 [MPa]: 6.21
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in3 | ASTM D792 | ||
| Filler Content | 0.00 % | 0.00 % | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 114 MPa | 16600 psi | ASTM D638 | ||
| Elongation at Break | 2.6 % | 2.6 % | ASTM D638 | ||
| 4.0 % | 4.0 % | Flexural Strain; ASTM D790 | |||
| Tensile Modulus | 5.52 GPa | 800 ksi | ASTM D638 | ||
| Flexural Strength | 207 MPa | 30000 psi | ASTM D790 | ||
| Flexural Modulus | 6.21 GPa | 900 ksi | ASTM D790 | ||
| Compressive Strength | 181 MPa | 26300 psi | 10% Deformation; ASTM D695 | ||
| Compressive Modulus | 3.79 GPa | 550 ksi | ASTM D695 | ||
| Izod Impact, Notched | 0.571 J/cm | 1.07 ft-lb/in | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 386 °C | 726 °F | DSC | ||
| Descriptive Properties | |||||
| Color | Tan | ||||