- 拉伸強度 [MPa]: 8.158
- 脆化溫度 [℃]: -27.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | 23°C; ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 56 | 56 | in Air 302°F, 168 hr; ASTM D573 | ||
| 51 @Thickness 2.00 mm, Time 15.0 sec | 51 @Thickness 0.0787 in, Time 0.00417 hour | Across Flow; ISO 868 | |||
| Tensile Strength, Yield | 8.158 MPa | 1183 psi | 302°F, 168 hr; ASTM D573 | ||
| 12.0 MPa | 1740 psi | Across Flow; ASTM D638 | |||
| Elongation at Yield | 22.6 % | 22.6 % | 302°F, 168 hr; ASTM D573 | ||
| 31 % | 31 % | Across Flow; ASTm D638 | |||
| Tear Strength | 87.1 kN/m | 497 pli | 73°C, Die C; ASTM D624 | ||
| Compression Set | 59 % | 59 % | 158°F, 22 hr; ASTM D395 | ||
| 74 % | 74 % | 257°F, 70 hr; ASTM D395 | |||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 2.4 | 2.4 | 1.98 mm; ASTM D150 | ||
| Dielectric Strength | 30.7 kV/mm | 780 kV/in | 2.03 mm; ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | -27.8 °C | -18.0 °F | ASTM D746 | ||
| UL RTI, Electrical | 85.0 °C | 185 °F | UL 746 | ||
| UL RTI, Mechanical with Impact | 85.0 °C | 185 °F | UL 746 | ||
| Flammability, UL94 | HB @Thickness 1.00 mm | HB @Thickness 0.0394 in | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | ||||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 175 - 230 °C | 347 - 446 °F | |||
| Rear Barrel Temperature | 193 °C | 380 °F | |||
| Middle Barrel Temperature | 199 °C | 390 °F | |||
| Front Barrel Temperature | 204 °C | 400 °F | |||
| Nozzle Temperature | 210 - 241 °C | 410 - 465 °F | |||
| Die Temperature | 216 °C | 420 °F | Extrusion | ||
| Melt Temperature | 210 °C | 410 °F | Extrusion | ||
| 216 - 232 °C | 420 - 450 °F | Processing | |||
| Mold Temperature | 10.0 - 51.7 °C | 50.0 - 125 °F | Processing | ||
| Drying Temperature | 82.2 °C | 180 °F | |||
| Dry Time | 3 hour | 3 hour | |||
| Moisture Content | 0.080 % | 0.080 % | |||
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | Processing | ||
| 5.00 - 20.0 MPa | 725 - 2900 psi | Extrusion | |||
| Clamp Pressure | 41.4 - 68.9 MPa | 6000 - 10000 psi | |||
| Vent Depth | 0.00254 cm | 0.00100 in | |||
| Cushion | 0.317 - 0.635 cm | 0.125 - 0.250 in | |||
| Screw Speed | 100 - 200 rpm | 100 - 200 rpm | |||
| Descriptive Properties | |||||
| Color | Black | ||||
| Form | Pellets | ||||
| Injection Rate | Fast | ||||
| Maximum Regrind % | 20 | ||||
| Screw Compression Ratio | 2:1 - 2.5:1 | ||||
| Screw L/D Ratio | 16:1 - 20:1 | ||||