- 熔體流動速率 [g/10min]: 2.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 | ||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | at 200°C/5.0 kg; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 43 | 43 | ASTM D2240 | ||
| Tensile Strength at Break | 11.7 MPa | 1700 psi | 20 in/min; ASTM D412 | ||
| Tensile Stress | 0.621 MPa @Strain 100 % | 90.0 psi @Strain 100 % | 20 in/min; ASTM D412 | ||
| Elongation at Break | 740 % | 740 % | 20 in/min; ASTM D412 | ||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 182 - 232 °C | 360 - 450 °F | |||
| Middle Barrel Temperature | 188 - 238 °C | 370 - 460 °F | |||
| Front Barrel Temperature | 193 - 243 °C | 380 - 470 °F | |||
| Nozzle Temperature | 199 - 249 °C | 390 - 480 °F | |||
| Zone 1 | 182 - 232 °C | 360 - 450 °F | |||
| Zone 2 | 188 - 238 °C | 370 - 460 °F | |||
| Zone 3 | 193 - 243 °C | 380 - 470 °F | |||
| Zone 5 | 199 - 249 °C | 390 - 480 °F | |||
| Die Temperature | 199 - 249 °C | 390 - 480 °F | |||
| Melt Temperature | 199 - 249 °C | 390 - 480 °F | Processing Temperature | ||
| Mold Temperature | 35.0 - 48.9 °C | 95.0 - 120 °F | |||
| Injection Pressure | 1.38 - 5.52 MPa | 200 - 800 psi | |||
| Back Pressure | 0.172 - 0.689 MPa | 25.0 - 100 psi | |||
| Cushion | 0.381 - 2.54 cm | 0.150 - 1.00 in | |||
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm | |||
| Descriptive Properties | |||||
| Appearance | Natural Color | ||||