- 密度 [g/cm3]: 0.88
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.880 g/cc | 0.0318 lb/in3 | DIN EN ISO 1183-1:2004 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 55 | 55 | DIN 53505 / ISO 868 | ||
| Tensile Strength at Break | 10.0 MPa | 1450 psi | Deviating from ISO 37 standard test piece is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Elongation at Break | 835 % | 835 % | Deviating from ISO 37 standard test piece is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Graves Tear Strength | 15.5 kN/m | 88.4 pli | DIN ISO 34-1 Method B (b) | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 100 °C | 212 °F | with dynamic stress | ||
| 120 °C | 248 °F | static | |||
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |||
| Descriptive Properties | |||||
| Color | Translucent | ||||