- 密度 [g/cm3]: 1.12
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in3 | DIN EN ISO 1183-1:2004 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 90 | 90 | DIN 53505 / ISO 868 | ||
| Tensile Strength at Break | 5.00 MPa | 725 psi | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Elongation at Break | 400 % | 400 % | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Graves Tear Strength | 30.0 kN/m | 171 pli | DIN ISO 34-1 Method B (b) | ||
| Compression Set | 27 % @Temperature 23.0 °C, Time 259000 sec | 27 % @Temperature 73.4 °F, Time 72.0 hour | ISO 815 | ||
| 55 % @Temperature 70.0 °C, Time 79200 sec | 55 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 77 % @Temperature 100 °C, Time 79200 sec | 77 % @Temperature 212 °F, Time 22.0 hour | ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Flammability, UL94 | V-0 | V-0 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 180 - 220 °C | 356 - 428 °F | |||
| Drying Temperature | 80.0 °C @Time 7200 sec | 176 °F @Time 2.00 hour | Pre drying | ||
| Descriptive Properties | |||||
| Color | Black | ||||