- 密度 [g/cm3]: 0.982
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.982 g/cc | 0.0355 lb/in3 | DIN EN ISO 1183-1:2004 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 73 | 73 | DIN 53505 / ISO 868 | ||
| Tensile Strength at Break | 8.00 MPa | 1160 psi | Deviating from ISO 37 standard test piece is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Elongation at Break | 580 % | 580 % | Deviating from ISO 37 standard test piece is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Graves Tear Strength | 16.5 kN/m | 94.1 pli | DIN ISO 34-1 Method B (b) | ||
| Compression Set | 29 % @Temperature 23.0 °C, Time 259000 sec | 29 % @Temperature 73.4 °F, Time 72.0 hour | ISO 815 | ||
| 50 % @Temperature 70.0 °C, Time 79200 sec | 50 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 78 % @Temperature 100 °C, Time 79200 sec | 78 % @Temperature 212 °F, Time 22.0 hour | ISO 815 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 180 - 250 °C | 356 - 482 °F | |||
| Descriptive Properties | |||||
| Color | Black | ||||