- 密度 [g/cm3]: 1.05
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in3 | DIN EN ISO 1183-1:2004 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 80 | 80 | DIN 53505 / ISO 868 | ||
| Tensile Strength at Break | 11.0 MPa | 1600 psi | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Elongation at Break | 480 % | 480 % | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504 / ISO 37 | ||
| Graves Tear Strength | 23.0 kN/m | 131 pli | DIN ISO 34-1 Method B (b) | ||
| Compression Set | 19 % @Temperature 23.0 °C, Time 259000 sec | 19 % @Temperature 73.4 °F, Time 72.0 hour | ISO 815 | ||
| 37 % @Temperature 70.0 °C, Time 86400 sec | 37 % @Temperature 158 °F, Time 24.0 hour | ISO 815 | |||
| 41 % @Temperature 100 °C, Time 86400 sec | 41 % @Temperature 212 °F, Time 24.0 hour | ISO 815 | |||
| 48 % @Temperature 120 °C, Time 86400 sec | 48 % @Temperature 248 °F, Time 24.0 hour | ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | <= 140 °C | <= 284 °F | |||
| Descriptive Properties | |||||
| Color | Natural | ||||