- 密度 [g/cm3]: 0.89
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.890 g/cc | 0.0322 lb/in3 | DIN 53479 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 80 | 80 | DIN 53505 | ||
| Tensile Strength at Break | 16.0 MPa | 2320 psi | DIN 53504 | ||
| Elongation at Break | 780 % | 780 % | DIN 53504 | ||
| Tear Strength | 28.0 kN/m | 160 pli | DIN 53515 | ||
| Taber Abrasion, mg/1000 Cycles | 45 | 45 | mm3; DIN 53516 | ||
| Compression Set | 50 % | 50 % | 72 hours at 23°C; ISO 815 | ||
| 70 % | 70 % | 24 hours at -25°C; ISO 815 | |||
| 90 % @Temperature 70.0 °C | 90 % @Temperature 158 °F | 24 hours; ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |||
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 160 - 180 °C | 320 - 356 °F | |||
| Descriptive Properties | |||||
| Color | Transparent | ||||
| Compression Ratio | 3.5:1 | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.