- 密度 [g/cm3]: 0.89
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.890 g/cc | 0.0322 lb/in3 | DIN 53479 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 85 | 85 | DIN 53505 | ||
| Tensile Strength at Break | 18.5 MPa | 2680 psi | Deviating from ISO 37 standard test piece is tested with a traverse speed of 200 mm/min; DIN 53504 | ||
| Elongation at Break | 700 % | 700 % | Deviating from ISO 37 standard test piece is tested with a traverse speed of 200 mm/min; DIN 53504 | ||
| Tear Strength | 39.0 kN/m | 223 pli | DIN 53515 | ||
| Compression Set | 36 % @Temperature 23.0 °C, Time 259000 sec | 36 % @Temperature 73.4 °F, Time 72.0 hour | ISO 815 | ||
| 55 % @Temperature 70.0 °C, Time 79200 sec | 55 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 75 % @Temperature 100 °C, Time 79200 sec | 75 % @Temperature 212 °F, Time 22.0 hour | ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | |||
| Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified | ||
| Descriptive Properties | |||||
| Color | Transparent | ||||