- 密度 [g/cm3]: 1.2
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in3 | DIN 53479 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 45 | 45 | DIN 53505 | ||
| Tensile Strength at Break | 3.30 MPa | 479 psi | DIN 53504 | ||
| Elongation at Break | 357 % | 357 % | DIN 53504 | ||
| Tear Strength | 12.1 kN/m | 69.0 pli | DIN 53515 | ||
| Compression Set | 36 % | 36 % | 72 hours at 23°C; ISO 815 | ||
| 87 % @Temperature 70.0 °C | 87 % @Temperature 158 °F | 24 hours; ISO 815 | |||
| 89 % @Temperature 100 °C | 89 % @Temperature 212 °F | 24 hours; ISO 815 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 240 - 270 °C | 464 - 518 °F | For adhesion to PA 6 | ||
| 255 - 280 °C | 491 - 536 °F | For adhesion to PA 66 and Polyarylamide | |||
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |||
| Drying Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Pre-drying | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | Pre-drying | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.