- 密度 [g/cm3]: 1.13
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | DIN 53479 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 67 | 67 | DIN 53505 | ||
| Tensile Strength at Break | 5.00 MPa | 725 psi | Preliminary value; DIN 53504 | ||
| Elongation at Break | 450 % | 450 % | Preliminary value; DIN 53504 | ||
| Tear Strength | 22.0 kN/m | 126 pli | Preliminary value; DIN 53515 | ||
| Compression Set | 35 % | 35 % | 72 hours at 23°C, preliminary value; ISO 815 | ||
| 70 % @Temperature 70.0 °C | 70 % @Temperature 158 °F | 24 hours at 70°C, preliminary value; ISO 815 | |||
| 78 % @Temperature 100 °C | 78 % @Temperature 212 °F | 24 hours at 100°C, preliminary value; ISO 815 | |||
| Thermal Properties | Metric | English | Comments | ||
| Flammability, UL94 | HB | HB | Yellow card | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 180 - 240 °C | 356 - 464 °F | |||
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |||
| Drying Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Pre-drying | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | Pre-drying | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.