- 密度 [g/cm3]: 1.1
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in3 | DIN e | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 61 | 61 | DIN 53505 / ISO 868 | ||
| Tensile Strength at Break | 4.20 MPa | 609 psi | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504/ ISO 37 | ||
| Elongation at Break | 530 % | 530 % | Deviating from ISO 37 standard test piece S2 is tested with a traverse speed of 200 mm/min; DIN 53504/ ISO 37 | ||
| Tear Strength | 20.0 kN/m | 114 pli | ISO 34-1 method B (b) | ||
| Compression Set | 22 % @Temperature 23.0 °C, Time 259000 sec | 22 % @Temperature 73.4 °F, Time 72.0 hour | ISO 815 | ||
| 77 % @Temperature 70.0 °C, Time 79200 sec | 77 % @Temperature 158 °F, Time 22.0 hour | ISO 815 | |||
| 82 % @Temperature 100 °C, Time 79200 sec | 82 % @Temperature 212 °F, Time 22.0 hour | ISO 815 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 215 - 270 °C | 419 - 518 °F | |||
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | |||
| Drying Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Pre-drying | ||
| Dry Time | 2 - 4 hour | 2 - 4 hour | Pre-drying | ||
| Descriptive Properties | |||||
| Color | Natural | ||||