- 拉伸強度 [MPa]: 8.69
- 脆化溫度 [℃]: -62.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.950 g/cc | 0.950 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 75 | 75 | Instant; ASTM D2240 |
| Tensile Strength, Yield | 8.69 MPa | 1260 psi | Method A (Dumbbell & Section), 20 in/min, Break; ASTM D412 |
| 5.52 MPa @Strain 300 % | 800 psi @Strain 300 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 | |
| Elongation at Break | 570 % | 570 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 |
| Rebound | 46 % | 46 % | Bayshore; ASTM D2632 |
| Tear Strength | 50.8 kN/m | 290 pli | Die C (graves), 20 in/min; ASTM D624 |
| Compression Set | 20 % | 20 % | Method B, 73°F(23°C), 22 hrs; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -62.0 °C | -79.6 °F | ASTM D746 |