- 拉伸強度 [MPa]: 9.65
- 脆化溫度 [℃]: -60.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| 0.900 g/cc | 0.900 g/cc | ASTM D792 | |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 33 | 33 | 10 Sec; ASTM D2240 |
| 33 | 33 | 10 Sec; ASTM D2240 | |
| Tensile Strength, Yield | 9.65 MPa | 1400 psi | Method A (Dumbbell & Section), 20 in/min, Break; ASTM D412 |
| 9.65 MPa | 1400 psi | Method A (Dumbbell & Section), 20 in/min, Break; ASTM D412 | |
| 9.31 MPa @Strain 300 % | 1350 psi @Strain 300 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 | |
| 9.31 MPa @Strain 300 % | 1350 psi @Strain 300 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 | |
| Elongation at Break | 300 % | 300 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 |
| 300 % | 300 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 | |
| Rebound | 30 % | 30 % | Bayshore; ASTM D2632 |
| Tear Strength | 64.9 kN/m | 370 pli | Die C (graves), 20 in/min; ASTM D624 |
| 64.9 kN/m | 370 pli | Die C (graves), 20 in/min; ASTM D624 | |
| Compression Set | 41 % | 41 % | Method B, 73°F(23°C), 22 hrs; ASTM D395 |
| 41 % | 41 % | Method B, 73°F(23°C), 22 hrs; ASTM D395 | |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -60.0 °C | -76.0 °F | ASTM D746 |