- 拉伸強度 [MPa]: 5.72
- 脆化溫度 [℃]: -65.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| 0.900 g/cc | 0.900 g/cc | ASTM D792 | |
| Linear Mold Shrinkage | 0.0125 cm/cm | 0.0125 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 61 | 61 | Instant; ASTM D2240 |
| 61 | 61 | Instant; ASTM D2240 | |
| Tensile Strength, Yield | 5.72 MPa | 830 psi | Method A (Dumbbell & Section), 20 in/min, Break; ASTM D412 |
| 5.72 MPa | 830 psi | Method A (Dumbbell & Section), 20 in/min, Break; ASTM D412 | |
| 3.79 MPa @Strain 300 % | 550 psi @Strain 300 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 | |
| Elongation at Break | 620 % | 620 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 |
| 620 % | 620 % | Method A (Dumbbell & Section), 20 in/min; ASTM D412 | |
| Rebound | 50 % | 50 % | Bayshore; ASTM D2632 |
| Tear Strength | 35.1 kN/m | 200 pli | Die C (graves), 20 in/min; ASTM D624 |
| Compression Set | 20 % | 20 % | Method B, 73°F(23°C), 22 hrs; ASTM D395 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -65.0 °C | -85.0 °F | ASTM D746 |