- 密度 [g/cm3]: 1.32
- 缺口沖擊強度: 0.53
- 拉伸強度 [MPa]: 173.0
- 彎曲模量 [MPa]: 16.54
- 熱變形溫度 [℃]: 222.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in3 | ASTM D792 |
| 1.32 g/cc | 0.0477 lb/in3 | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0035 cm/cm @Time 86400 sec | 0.0035 in/in @Time 24.0 hour | ISO 294 |
| 0.0040 cm/cm @Time 86400 sec | 0.0040 in/in @Time 24.0 hour | ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Time 86400 sec | 0.0080 in/in @Time 24.0 hour | ASTM D955 |
| 0.0080 cm/cm @Time 86400 sec | 0.0080 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 173 MPa | 25100 psi | ASTM D638 |
| 188 MPa | 27300 psi | ISO 527 | |
| Tensile Strength, Yield | 173 MPa | 25100 psi | ASTM D638 |
| 188 MPa | 27300 psi | ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| 6.2 % | 6.2 % | ISO 527 | |
| Elongation at Yield | 1.9 % | 1.9 % | ISO 527 |
| 2.0 % | 2.0 % | ASTM D638 | |
| Tensile Modulus | 19.2 GPa | 2780 ksi | 1 mm/min; ISO 527 |
| 19.85 GPa | 2879 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 282 MPa | 40900 psi | ASTM D790 |
| 289 MPa | 41900 psi | ISO 178 | |
| Flexural Modulus | 16.54 GPa | 2399 ksi | ASTM D790 |
| 17.0 GPa | 2470 ksi | ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.01 J/cm | 15.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 | 3.33 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 49.0 kJ/m2 | 23.3 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J | 4.43 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.46 | 0.46 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.46 | 0.46 | ASTM D3702 Modified |
| K (wear) Factor | 30.2 x 10-8 mm3/N-M | 15.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 48.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 26.7 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 48.6 μm/m-°C @Temperature -40.0 - 40.0 °C | 27.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| CTE, linear, Transverse to Flow | 25.2 μm/m-°C @Temperature -40.0 - 40.0 °C | 14.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 26.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 14.4 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 221 °C @Thickness 3.20 mm | 430 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 212 °C @Thickness 3.20 mm | 414 °F @Thickness 0.126 in | unannealed; ASTM D648 | |