- 密度 [g/cm3]: 1.37
- 缺口沖擊強度: 2.4
- 彎曲模量 [MPa]: 7.97
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in3 | ASTM D792 |
| 1.37 g/cc | 0.0495 lb/in3 | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| 0.190 % | 0.190 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec | 0.0010 - 0.0030 in/in @Time 24.0 hour | ASTM D955 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec | 0.0010 - 0.0030 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec | 0.0080 - 0.010 in/in @Time 24.0 hour | ASTM D955 |
| 0.0080 - 0.010 cm/cm @Time 86400 sec | 0.0080 - 0.010 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 122 MPa | 17700 psi | ASTM D638 |
| 123 MPa | 17800 psi | ISO 527 | |
| Elongation at Break | 3.9 % | 3.9 % | ISO 527 |
| 4.9 % | 4.9 % | ASTM D638 | |
| Tensile Modulus | 7.60 GPa | 1100 ksi | 1 mm/min; ISO 527 |
| 9.28 GPa | 1350 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 192 MPa | 27800 psi | ISO 178 |
| 220 MPa | 31900 psi | ASTM D790 | |
| Flexural Modulus | 7.97 GPa | 1160 ksi | ISO 178 |
| 8.48 GPa | 1230 ksi | ASTM D790 | |
| Izod Impact, Notched | 2.40 J/cm | 4.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 12.28 J/cm | 23.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 21.0 kJ/m2 | 9.99 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m2 | 35.7 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 18.0 J | 13.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 28.8 μm/m-°C @Temperature -40.0 - 40.0 °C | 16.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 30.4 μm/m-°C @Temperature -40.0 - 40.0 °C | 16.9 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 88.2 μm/m-°C @Temperature -40.0 - 40.0 °C | 49.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 88.7 μm/m-°C @Temperature -40.0 - 40.0 °C | 49.3 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 177 °C @Thickness 3.20 mm | 351 °F @Thickness 0.126 in | unannealed; ASTM D648 | |