- 密度 [g/cm3]: 1.16
- 缺口沖擊強度: 15.0
- 彎曲模量 [MPa]: 3.54
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in3 | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 81.0 MPa | 11700 psi | ISO 527 |
| Elongation at Break | 12.2 % | 12.2 % | ISO 527 |
| Tensile Modulus | 3.67 GPa | 532 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 100 MPa | 14500 psi | ISO 178 |
| Flexural Modulus | 3.54 GPa | 513 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m2 | 7.14 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m2 | 35.7 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |