- 拉伸強度 [MPa]: 14.1
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Tensile Strength at Break | 30.5 MPa | 4420 psi | 60% Ret. | ||
| Tensile Strength, Yield | 14.1 MPa | 2050 psi | 34% Ret. | ||
| Elongation at Break | 124 % | 124 % | 155% Ret. | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 230 °C | 446 °F | Flange Temperature for T-Die Cast Film Extrusion | ||
| Zone 1 | 190 °C | 374 °F | For T-Die Cast Film Extrusion | ||
| 230 °C | 446 °F | For 8x1 mm Tube Extrusion | |||
| Zone 2 | 210 °C | 410 °F | For T-Die Cast Film Extrusion | ||
| 225 °C | 437 °F | For 8x1 mm Tube Extrusion | |||
| Zone 3 | 220 °C | 428 °F | For 8x1 mm Tube Extrusion | ||
| 230 °C | 446 °F | For T-Die Cast Film Extrusion | |||
| Zone 4 | 215 °C | 419 °F | For 8x1 mm Tube Extrusion | ||
| Die Temperature | 230 °C | 446 °F | For T-Die Cast Film Extrusion | ||
| Die Opening | 0.0400 cm | 0.0157 in | For T-Die Cast Film Extrusion | ||
| Roll Temperature | 50.0 °C | 122 °F | Chill Roll Temperature for T-Die Cast Film Extrusion | ||
| Drying Temperature | 80.0 °C | 176 °F | Option 1 | ||
| 100 °C | 212 °F | Option 2 | |||
| 110 °C | 230 °F | Option 3 | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | Option 3 | ||
| 4 - 6 hour | 4 - 6 hour | Option 2 | |||
| 6 - 8 hour | 6 - 8 hour | Option 1 | |||
| Screw Speed | 15 - 76 rpm | 15 - 76 rpm | For 8x1 mm Tube Extrusion | ||
| Descriptive Properties | |||||
| C/R | 3-3.5:1 | For 8x1 mm Tube Extrusion | |||
| Calibrating Vacuum | 100 mbar | For 8x1 mm Tube Extrusion | |||
| Calibration | 9.95 mm | For 8x1 mm Tube Extrusion | |||
| Compression Ratio | min 3:1 | For 8x1 mm Tube Extrusion | |||
| Die Diameter | 16 mm | For 8x1 mm Tube Extrusion | |||
| Die Width | 300 mm | For T-Die Cast Film Extrusion | |||
| Extruder | Barmag, Screw Diameter = 30 mm | For T-Die Cast Film Extrusion | |||
| Extruder Characteristics | 65 mm screw diameter | For 8x1 mm Tube Extrusion | |||
| Film Thickness | 60 microns | For T-Die Cast Film Extrusion | |||
| Haul Off Speed | 5 m/min | For T-Die Cast Film Extrusion | |||
| Haul Speed | 10-55 m/min | For 8x1 mm Tube Extrusion | |||
| L/D Ratio | 25:1 | For 8x1 mm Tube Extrusion | |||
| Length of Compression Zone | 30% of screw length | For 8x1 mm Tube Extrusion | |||
| Length of Feeding Zone | 30-40% of screw length | For 8x1 mm Tube Extrusion | |||
| Length of Metering Zone | 30-45% of screw length | For 8x1 mm Tube Extrusion | |||
| Mandrel Diameter | 12 mm | For 8x1 mm Tube Extrusion | |||
| Tensile Work To Break | 673 kJ/m2 | 83% Ret. | |||
| Water Temperature | 10-18°C | For 8x1 mm Tube Extrusion | |||