- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 0.25
- 缺口沖擊強(qiáng)度: 1.33
- 拉伸強(qiáng)度 [MPa]: 51.0
- 彎曲模量 [MPa]: 1.21
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in3 | ASTM D792 |
| Water Absorption | 0.25 % @Time 86400 sec | 0.25 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.010 cm/cm @Thickness 3.17 mm | 0.010 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 81.4 MPa | 11800 psi | ASTM D790 |
| Flexural Modulus | 1.21 GPa | 175 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm @Thickness 3.17 mm | 2.50 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 100 ohm-cm | 100 ohm-cm | ASTM D257 |
| Surface Resistance | 1000 ohm | 1000 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 16.2 μm/m-°C | 9.00 μin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.4 °C | 130 °F | Unannealed; ASTM D648 |