- 密度 [g/cm3]: 1.07
- 缺口沖擊強度: 0.85
- 拉伸強度 [MPa]: 104.0
- 彎曲模量 [MPa]: 6.20
- 熱變形溫度 [℃]: 176.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in3 | ASTM D792 |
| 1.08 g/cc | 0.0390 lb/in3 | ISO 1183 | |
| Moisture Absorption | 0.100 % | 0.100 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec | 0.0010 - 0.0030 in/in @Time 24.0 hour | ASTM D955 |
| 0.0030 cm/cm @Time 86400 sec | 0.0030 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm @Time 86400 sec | 0.0050 in/in @Time 24.0 hour | ISO 294 |
| 0.0060 - 0.0080 cm/cm @Time 86400 sec | 0.0060 - 0.0080 in/in @Time 24.0 hour | ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 104 MPa | 15100 psi | ASTM D638 |
| 120 MPa | 17400 psi | ISO 527 | |
| Tensile Strength, Yield | 104 MPa | 15100 psi | ASTM D638 |
| Elongation at Break | 3.9 % | 3.9 % | ASTM D638 |
| 4.0 % | 4.0 % | ISO 527 | |
| Elongation at Yield | 3.8 % | 3.8 % | ASTM D638 |
| Tensile Modulus | 7.58 GPa | 1100 ksi | 50 mm/min; ASTM D638 |
| 8.70 GPa | 1260 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 6.20 GPa | 899 ksi | ASTM D790 |
| 7.00 GPa | 1020 ksi | ISO 178 | |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.26 J/cm | 13.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 11.0 kJ/m2 | 5.23 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Dart Drop, Total Energy | 13.0 J | 9.59 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 100 - 1.00e+6 ohm | 100 - 1.00e+6 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 88.2 μm/m-°C @Temperature -40.0 - 40.0 °C | 49.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| CTE, linear, Transverse to Flow | 28.8 μm/m-°C @Temperature -40.0 - 40.0 °C | 16.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 176 °C @Thickness 3.20 mm | 349 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 162 °C @Thickness 3.20 mm | 324 °F @Thickness 0.126 in | unannealed; ASTM D648 | |