- 密度 [g/cm3]: 1.02
- 吸水率 [%]: 0.2
- 缺口沖擊強(qiáng)度: 1.6
- 拉伸強(qiáng)度 [MPa]: 57.0
- 彎曲模量 [MPa]: 1.10
- 硬度: 100.0
- 熱變形溫度 [℃]: 135.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in3 | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hrs; ASTM D570 |
| Water Absorption at Saturation | 1.4 % | 1.4 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 100 | 100 | ASTM D785 |
| Tensile Strength, Yield | 57.0 MPa | 8270 psi | ASTM D638 |
| Elongation at Break | 395 % | 395 % | ASTM D638 |
| Flexural Modulus | 1.10 GPa | 160 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm | 3.00 ft-lb/in | ASTM D256 |
| 1.10 J/cm @Temperature -40.0 °C | 2.06 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 184 °C | 363 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ASTM D648 |
- 關(guān)鍵詞:
- 供應(yīng)
- PA12
- Ashley Polymers Ashlene? D925 Nylon 12