- 密度 [g/cm3]: 1.01
- 吸水率 [%]: 1.8
- 拉伸強度 [MPa]: 45.0
- 熱變形溫度 [℃]: 80.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in3 | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.80 % @Thickness 1.00 mm, Temperature 23.0 °C | 0.80 % @Thickness 0.0394 in, Temperature 73.4 °F | 50% R.H.; ISO 62 | ||
| Water Absorption at Saturation | 1.8 % @Thickness 1.00 mm | 1.8 % @Thickness 0.0394 in | ISO 62 | ||
| Linear Mold Shrinkage | 0.014 cm/cm | 0.014 in/in | 127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2) | ||
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | 127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2) | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ISO 527-1/2 | ||
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-1/2 | ||
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527-1/2 | ||
| Tensile Modulus | 1.30 GPa | 189 ksi | ISO 527-1/2 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.700 J/cm2 @Temperature -30.0 °C | 3.33 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.700 J/cm2 @Temperature 23.0 °C | 3.33 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.0 @Frequency 1e+6 Hz | 3.0 @Frequency 1e+6 Hz | IEC 60250 | ||
| 3.7 @Frequency 100 Hz | 3.7 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | K20/P50; IEC 60243-1 | ||
| Dissipation Factor | 0.028 @Frequency 1e+6 Hz | 0.028 @Frequency 1e+6 Hz | IEC 60250 | ||
| 0.045 @Frequency 100 Hz | 0.045 @Frequency 100 Hz | IEC 60250 | |||
| Comparative Tracking Index | >= 600 V | >= 600 V | Test Solution A, 50 drops; IEC 60112 | ||
| 600 V | 600 V | Test Solution A, 100 drops; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 150 μm/m-°C @Temperature 23.0 - 55.0 °C | 83.3 μin/in-°F @Temperature 73.4 - 131 °F | 45x15x10 mm; ISO 11359 | ||
| Melting Point | 175 °C | 347 °F | Peak Temperature; ISO 3146, ISO 11357 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 40.0 °C | 104 °F | ISO 75 | ||
| Vicat Softening Point | 130 °C | 266 °F | 50N; ISO 306 | ||
| 170 °C | 338 °F | 10N; ISO 306 | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||||
| Descriptive Properties | |||||
| Electrolytic Corrosion | A1 Step | IEC 60426 | |||