- 密度 [g/cm3]: 1.24
- 吸水率 [%]: 1.1
- 拉伸強度 [MPa]: 69.0
- 熱變形溫度 [℃]: 170.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in3 | ISO 1183 | ||
| Moisture Absorption at Equilibrium | 0.50 % @Thickness 1.00 mm, Temperature 23.0 °C | 0.50 % @Thickness 0.0394 in, Temperature 73.4 °F | 50% R.H.; ISO 62 | ||
| Water Absorption at Saturation | 1.1 % @Thickness 1.00 mm | 1.1 % @Thickness 0.0394 in | ISO 62 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | 127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2) | ||
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | 127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2) | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527-1/2 | ||
| Tensile Strength, Yield | 69.0 MPa | 10000 psi | ISO 527-1/2 | ||
| Elongation at Break | 10 % | 10 % | ISO 527-1/2 | ||
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1/2 | ||
| Tensile Modulus | 4.00 GPa | 580 ksi | ISO 527-1/2 | ||
| Charpy Impact Unnotched | 6.50 J/cm2 @Temperature -30.0 °C | 30.9 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 7.00 J/cm2 @Temperature 23.0 °C | 33.3 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm2 @Temperature 23.0 °C | 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| 1.10 J/cm2 @Temperature -30.0 °C | 5.24 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.4 @Frequency 1e+6 Hz | 3.4 @Frequency 1e+6 Hz | IEC 60250 | ||
| 4.1 @Frequency 100 Hz | 4.1 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | K20/P50; IEC 60243-1 | ||
| Dissipation Factor | 0.024 @Frequency 1e+6 Hz | 0.024 @Frequency 1e+6 Hz | IEC 60250 | ||
| 0.031 @Frequency 100 Hz | 0.031 @Frequency 100 Hz | IEC 60250 | |||
| Comparative Tracking Index | >= 600 V | >= 600 V | Test Solution A, 50 drops; IEC 60112 | ||
| 600 V | 600 V | Test Solution A, 100 drops; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 50.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 27.8 μin/in-°F @Temperature 73.4 - 131 °F | 45x15x10 mm; ISO 11359 | ||
| Melting Point | 178 °C | 352 °F | Peak Temperature; ISO 3146, ISO 11357 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ISO 75 | ||
| Vicat Softening Point | 170 °C | 338 °F | 50N; ISO 306 | ||
| 175 °C | 347 °F | 10N; ISO 306 | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||||
| Descriptive Properties | |||||
| Electrolytic Corrosion | A1 Step | IEC 60426 | |||