- 熔體流動速率 [g/10min]: 14.0
- 密度 [g/cm3]: 1.12
- 缺口沖擊強度: 0.24
- 拉伸強度 [MPa]: 65.0
- 斷裂伸長率 [%]: 85.0
- 彎曲模量 [MPa]: 2.50
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.12 - 1.14 g/cc | 0.0405 - 0.0412 lb/in3 | ASTM D792 | ||
| Apparent Bulk Density | >= 0.659 g/cc | >= 0.0238 lb/in3 | |||
| Viscosity Measurement | 2.7 | 2.7 | Relative Viscosity | ||
| Melt Flow | 14 - 20 g/10 min @Load 2.16 kg, Temperature 230 °C | 14 - 20 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | >= 65.0 MPa | >= 9430 psi | ASTM D638 | ||
| Elongation at Yield | <= 6.0 % | <= 6.0 % | ASTM D638 | ||
| Flexural Yield Strength | >= 85.0 MPa | >= 12300 psi | ASTM D790 | ||
| Flexural Modulus | >= 2.50 GPa | >= 363 ksi | ASTM D790 | ||
| Izod Impact, Notched | >= 0.240 J/cm | >= 0.450 ft-lb/in | ASTM D256, Notch | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 - 224 °C | 428 - 435 °F | ASTM DSC | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 55.0 °C | >= 131 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Moisture Content | <= 0.080 % | <= 0.080 % | |||
| Descriptive Properties | |||||
| Extractables, wt% | <0.4 | ||||