- 缺口沖擊強(qiáng)度: 1.07
- 拉伸強(qiáng)度 [MPa]: 51.7
- 斷裂伸長率 [%]: 89.6
- 彎曲模量 [MPa]: 2.76
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | ASTM D638 |
| Flexural Yield Strength | 89.6 MPa | 13000 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C | 2.00 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Surface Resistivity per Square | 1.00e+6 - 9.00e+9 ohm | 1.00e+6 - 9.00e+9 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 243 - 279 °C | 470 - 535 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Dry Time | 2 - 4 hour @Temperature 121 °C | 2 - 4 hour @Temperature 250 °F | to ensure moisture content is less than 0.02% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm | |