- 缺口沖擊強度: 9.08
- 拉伸強度 [MPa]: 40.0
- 彎曲模量 [MPa]: 1.03
- 熱變形溫度 [℃]: 97.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ASTM D638 |
| Elongation at Yield | 350 % | 350 % | ASTM D638 |
| Flexural Modulus | 1.03 GPa | 150 ksi | ASTM D790 |
| Izod Impact, Notched | 9.08 J/cm @Temperature 22.8 °C | 17.0 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 210 - 212 °C | 410 - 413 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.8 °C | 208 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 37.8 °C | 100 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 249 - 266 °C | 480 - 510 °F | |
| Middle Barrel Temperature | 249 - 266 °C | 480 - 510 °F | |
| Front Barrel Temperature | 254 - 271 °C | 490 - 520 °F | |
| Nozzle Temperature | 254 - 274 °C | 490 - 525 °F | |
| Melt Temperature | 254 - 271 °C | 490 - 520 °F | |
| Mold Temperature | 51.7 - 79.4 °C | 125 - 175 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C | 2 - 4 hour @Temperature 175 °F | to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.14 - 6.21 MPa | 600 - 900 psi | Secondary |
| 6.89 - 10.3 MPa | 1000 - 1500 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm | |