- 密度 [g/cm3]: 1.5
- 缺口沖擊強度: 1.33
- 彎曲模量 [MPa]: 11.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in3 | ASTM D792 |
| Filler Content | 40 % | 40 % | |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell E | 60 | 60 | ASTM D785 |
| Tensile Strength at Break | 193 MPa | 28000 psi | ASTM D638 |
| Elongation at Break | 1.0 % | 1.0 % | ASTM D638 |
| Flexural Strength | 283 MPa | 41000 psi | ASTM D790 |
| Flexural Modulus | 11.7 GPa | 1700 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm | 2.50 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 216 °C | 420 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 218 °C | 425 °F | Unannealed; ASTM D648 |