- 密度 [g/cm3]: 1.51
- 拉伸強度 [MPa]: 140.0
- 彎曲模量 [MPa]: 8.70
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in3 | |||
| Density | 1.51 g/cc | 0.0546 lb/in3 | ISO 1183 | ||
| Viscosity Measurement | 142 | 142 | ISO 307 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 250 MPa @Load 3.06 kg | 36300 psi @Load 6.74 lb | 358; ISO 2039-2 | ||
| Tensile Strength, Yield | 140 MPa | 20300 psi | ISO 527-2 | ||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-2 | ||
| Tensile Modulus | 10.5 GPa | 1520 ksi | ISO 527-2 | ||
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 | ||
| Flexural Modulus | 8.70 GPa | 1260 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 5.00 J/cm2 @Temperature 23.0 °C | 23.8 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.600 J/cm2 @Temperature 23.0 °C | 2.86 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ISO 3146 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75-2 | ||
| Decomposition Temperature | >= 300 °C | >= 572 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 270 °C | 518 °F | Feed Zone | ||
| Zone 2 | 280 °C | 536 °F | Compression | ||
| Zone 3 | 290 °C | 554 °F | Metering-zone | ||
| Zone 4 | 290 °C | 554 °F | Nozzle | ||
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | Injection Molding/Extrusion | ||
| 290 °C | 554 °F | Optimal | |||
| Mold Temperature | 80.0 °C | 176 °F | Optimal | ||
| 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding/Extrusion | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal | ||
| <= 0.15 % | <= 0.15 % | ||||
| Descriptive Properties | |||||
| Color | BK 00130 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >400°C | ASTM D1929 | |||
| Peripheral Screw Speed | < 0.3 m/s | ||||