- 熔體流動速率 [g/10min]: 68.0
- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 6.3
- 缺口沖擊強度: 20.0
- 彎曲模量 [MPa]: 5.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in3 | |||
| Density | 1.36 g/cc | 0.0491 lb/in3 | ISO 1183 | ||
| Water Absorption | 6.3 - 6.9 % | 6.3 - 6.9 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.9 - 2.3 % | 1.9 - 2.3 % | ISO 62 | ||
| Viscosity Measurement | 140 | 140 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | |||
| Melt Flow | 68 g/10 min @Load 5.00 kg, Temperature 275 °C | 68 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527-1/-2 | ||
| Elongation at Break | 8.0 % | 8.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 6.20 GPa | 899 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 | ||
| Flexural Modulus | 5.00 GPa | 725 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 20.0 kJ/m2 @Temperature 23.0 °C | 9.52 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | ||
| Charpy Impact Unnotched | 11.0 J/cm2 @Temperature 23.0 °C | 52.3 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 3.00 J/cm2 @Temperature 23.0 °C | 14.3 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 6.8 @Frequency 1.00e+6 Hz | 6.8 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.022 @Frequency 1.00e+6 Hz | 0.022 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 575 V | 575 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 0.360 W/m-K | 2.50 BTU-in/hr-ft2-°F | DIN 52612-1 | ||
| Melting Point | 220 °C | 428 °F | ISO 11357-1/-3 | ||
| Maximum Service Temperature, Air | 135 °C | 275 °F | for 50% loss of tensile strength after 20000hr | ||
| 165 °C | 329 °F | for 50% loss of tensile strength after 5000hr | |||
| 200 °C | 392 °F | ||||
| Decomposition Temperature | >= 300 °C | >= 572 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection Molding/Extrusion | ||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding | ||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >400°C | ASTM D1929 | |||