- 熔體流動速率 [g/10min]: 41.75
- 密度 [g/cm3]: 1.67
- 吸水率 [%]: 4.1
- 缺口沖擊強(qiáng)度: 2.5
- 拉伸強(qiáng)度 [MPa]: 110.0
- 彎曲模量 [MPa]: 10.0
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.67 g/cc | 0.0603 lb/in3 | ISO 1183 | ||
| Water Absorption | 4.1 - 4.7 % | 4.1 - 4.7 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.0 - 1.4 % | 1.0 - 1.4 % | 23°C; 50% RH; ISO 62 | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | restricted | ||
| Melt Flow | 41.75 g/10 min @Load 5.00 kg, Temperature 275 °C | 41.75 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 110 MPa | 16000 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 1.8 % | 1.8 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 11.0 GPa | 1600 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 165 MPa | 23900 psi | at max force; ISO 178 | ||
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 2.50 kJ/m2 @Temperature 23.0 °C | 1.19 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A | ||
| 4.50 kJ/m2 @Temperature -30.0 °C | 2.14 ft-lb/in2 @Temperature -22.0 °F | ISO 180/A | |||
| Charpy Impact Unnotched | 3.00 J/cm2 @Temperature 23.0 °C | 14.3 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | ||
| 3.00 J/cm2 @Temperature -30.0 °C | 14.3 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.250 J/cm2 @Temperature 23.0 °C | 1.19 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| 0.400 J/cm2 @Temperature -30.0 °C | 1.90 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 4.5 @Frequency 1.00 Hz | 4.5 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.015 @Frequency 1.00e+6 Hz | 0.015 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 40.0 - 60.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 22.2 - 33.3 μin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 40.0 - 50.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 22.2 - 27.8 μin/in-°F @Temperature 73.4 - 176 °F | DIN 11359-1/-2 | ||
| Specific Heat Capacity | 1.40 J/g-°C | 0.335 BTU/lb-°F | |||
| Thermal Conductivity | 1.00 W/m-K | 6.94 BTU-in/hr-ft2-°F | DIN 52612 | ||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 149 °C | 300 °F | for 50% loss of tensile strength after 20000hr | ||
| 167 °C | 333 °F | for 50% loss of tensile strength after 5000hr | |||
| 200 °C | 392 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | V-2 @Thickness >=0.750 mm | V-2 @Thickness >=0.0295 in | |||
| V-0 @Thickness >=1.50 mm | V-0 @Thickness >=0.0591 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 290 - 310 °C | 554 - 590 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Color | GR 22866 | ||||
| Commercial Status | Europe | ||||