- 缺口沖擊強度: 0.534
- 彎曲模量 [MPa]: 5.1951
- 熱變形溫度 [℃]: 211.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm @Thickness 3.175 mm | 0.010 in/in @Thickness 0.1250 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 119.89 MPa | 17388 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 149.86 MPa | 21735 psi | ASTM D790 |
| Flexural Modulus | 5.1951 GPa | 753.48 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 211 °C | 412 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 196 °C | 385 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 270 - 295 °C | 518 - 563 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |