- 熔體流動速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.25
- 吸水率 [%]: 0.6
- 彎曲強度 [MPa]: 130.0
- 彎曲模量 [MPa]: 7.00
- 熱變形溫度 [℃]: 210.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in3 | ISO R1183 | ||
| Water Absorption | 0.60 % | 0.60 % | 23°C / 24 hrs; ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | 23°C / 50% RH; ISO 62 | ||
| 2.3 % | 2.3 % | in 23°C water; ISO 62 | |||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 235 °C | 3.0 g/10 min @Load 4.76 lb, Temperature 455 °F | after drying; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 82 | 82 | ISO 868 | ||
| Tensile Strength, Ultimate | 130 MPa | 18900 psi | ISO R527 | ||
| Elongation at Break | 3.9 % | 3.9 % | ISO R527 | ||
| Modulus of Elasticity | 7.50 GPa | 1090 ksi | ISO R527 | ||
| Flexural Strength | 185 MPa | 26800 psi | After conditioning at 23°C and 50% RH; ISO 178 | ||
| 204 MPa | 29600 psi | Dry; ISO 178 | |||
| Flexural Modulus | 7.00 GPa | 1020 ksi | After conditioning at 23°C and 50% RH; ISO 178 | ||
| 7.40 GPa | 1070 ksi | Dry; ISO 178 | |||
| Charpy Impact, Notched | 2.20 J/cm2 | 10.5 ft-lb/in2 | After conditioning at 23°C/50%RH; ISO 179/Af | ||
| 2.00 J/cm2 @Temperature 23.0 °C | 9.52 ft-lb/in2 @Temperature 73.4 °F | Dry; ISO 179/Af | |||
| 18.0 J/cm2 @Temperature -20.0 °C | 85.7 ft-lb/in2 @Temperature -4.00 °F | Dry; ISO 179/Af | |||
| 19.0 J/cm2 @Temperature -20.0 °C | 90.4 ft-lb/in2 @Temperature -4.00 °F | After conditioning at 23°C/50%RH; ISO 179/Af | |||
| Tensile Creep Modulus, 1 hour | 5740 MPa | 833000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.30e+15 ohm-cm | 1.30e+15 ohm-cm | ASTM D257 | ||
| Surface Resistance | 1.30e+15 ohm | 1.30e+15 ohm | ASTM D257 | ||
| Dielectric Strength | 34.0 kV/mm @Thickness 1.00 mm | 864 kV/in @Thickness 0.0394 in | ASTM D149 | ||
| Dissipation Factor | 0.023 @Frequency 100000 Hz | 0.023 @Frequency 100000 Hz | NFC 26 230 | ||
| 0.064 @Frequency 100 Hz | 0.064 @Frequency 100 Hz | NFC 26 230 | |||
| 0.066 @Frequency 1000 Hz | 0.066 @Frequency 1000 Hz | NFC 26 230 | |||
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 19.0 μm/m-°C @Temperature 20.0 - 60.0 °C | 10.6 μin/in-°F @Temperature 68.0 - 140 °F | TMS2 Perkin Elmer | ||
| CTE, linear, Transverse to Flow | 120 μm/m-°C @Temperature 20.0 - 60.0 °C | 66.7 μin/in-°F @Temperature 68.0 - 140 °F | TMS2 Perkin Elmer | ||
| Melting Point | 220 °C | 428 °F | ISO R1218 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO R75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO R75 | ||
| Vicat Softening Point | 185 °C | 365 °F | 50 N - B method; ISO 306 | ||
| >= 210 °C | >= 410 °F | 10 N - A method; ISO 306 | |||
| Flammability, UL94 | HB | HB | |||
| Flammability Test | 6.0 | 6.0 | [mm/min] Burning Speed; FMVSS 302 | ||
| Descriptive Properties | |||||
| Automotive classification | D-3 | FMVSS 302 | |||