- 密度 [g/cm3]: 1.13
- 拉伸強(qiáng)度 [MPa]: 28.0
- 彎曲強(qiáng)度 [MPa]: 112.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0410 lb/in3 | Yield Density |
| Thickness | 50.8 microns | 2.00 mil | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 112 MPa | 16200 psi | ASTM D882 |
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D882 |
| Elongation at Break | 375 % | 375 % | ASTM D882 |
| Secant Modulus, MD | 0.517 GPa | 75.0 ksi | ASTM D882 |
| Tear Strength Test | 65 | 65 | grams/mil; ASTM D1922 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 218 - 220 °C | 424 - 428 °F | crystalline melting point; Hot Stage Microscope |
| Shrinkage | <= 2.0 % | <= 2.0 % | 0.5 hr. @ 300°F/149°C; ASTM D1204 |