- 缺口沖擊強度: 0.91
- 拉伸強度 [MPa]: 50.0
- 彎曲模量 [MPa]: 1.28
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.0010 | 0.0010 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ASTM D638 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 |
| Flexural Strength | 45.0 MPa | 6530 psi | ASTM D790 |
| Flexural Modulus | 1.28 GPa | 185 ksi | ASTM D790 |
| Izod Impact, Notched | 0.910 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |
| Middle Barrel Temperature | 240 - 255 °C | 464 - 491 °F | |
| Front Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |
| Die Temperature | 230 - 245 °C | 446 - 473 °F | |
| Melt Temperature | 250 - 260 °C | 482 - 500 °F | |
| Head Temperature | 230 - 245 °C | 446 - 473 °F | |