- 密度 [g/cm3]: 1.13
- 缺口沖擊強度: 0.534
- 拉伸強度 [MPa]: 69.98
- 彎曲模量 [MPa]: 2.699
- 硬度: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | MD; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 52.0 MPa | 7540 psi | ASTM D638 |
| Tensile Strength, Yield | 69.98 MPa | 10150 psi | ASTM D638 |
| Elongation at Break | 260 % | 260 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 1.80 GPa | 261 ksi | ASTM D638 |
| Flexural Strength | 107.0 MPa | 15520 psi | ASTM D790 |
| Flexural Modulus | 2.699 GPa | 391.5 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 235 °C | 455 °F | ASTM D789 |