- 密度 [g/cm3]: 1.15
- 吸水率 [%]: 8.0
- 缺口沖擊強度: 4.0
- 拉伸強度 [MPa]: 85.0
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in3 | ISO 1183 |
| Filler Content | 0.00 % | 0.00 % | ISO 3451 |
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | Humidity Absorption, 50% RH, 23°C; ISO 62 |
| Water Absorption at Saturation | 8.0 % | 8.0 % | 23°C; ISO 62 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | ISO 527 |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 3.20 GPa | 464 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 @Temperature -30.0 °C | 1.90 ft-lb/in2 @Temperature -22.0 °F | ISO 180/1A |
| 5.00 kJ/m2 @Temperature 23.0 °C | 2.38 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/eU |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/eU | |
| Charpy Impact, Notched | 0.400 J/cm2 @Temperature -30.0 °C | 1.90 ft-lb/in2 @Temperature -22.0 °F | ISO 179/eA |
| 0.500 J/cm2 @Temperature 23.0 °C | 2.38 ft-lb/in2 @Temperature 73.4 °F | ISO 179/eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 262 °C | 504 °F | 10 K/min; ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ISO 75-1/2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75-1/2 |
| Vicat Softening Point | 240 °C | 464 °F | 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||
| Glow Wire Test | 750 °C @Thickness 2.00 mm | 1380 °F @Thickness 0.0787 in | plaque; IEC 60695 |