- 密度 [g/cm3]: 1.43
- 缺口沖擊強度: 11.0
- 熱變形溫度 [℃]: 255.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in3 | ISO 1183 | ||
| Moisture Absorption | 1.50 % @Temperature 23.0 °C | 1.50 % @Temperature 73.4 °F | 50% RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | Eurotec | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | Eurotec | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 170 MPa | 24700 psi | ISO 527 | ||
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 | ||
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527 | ||
| Izod Impact, Notched (ISO) | 11.0 kJ/m2 @Temperature -30.0 °C | 5.23 ft-lb/in2 @Temperature -22.0 °F | ISO 180/1A | ||
| 13.0 kJ/m2 @Temperature 23.0 °C | 6.19 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m2 @Temperature -30.0 °C | 33.3 ft-lb/in2 @Temperature -22.0 °F | ISO 180/1U | ||
| 80.0 kJ/m2 @Temperature 23.0 °C | 38.1 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1U | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 262 °C | 504 °F | [10 K/min], ISO 11357 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75 | ||
| Vicat Softening Point | 250 °C @Load 5.10 kg | 482 °F @Load 11.2 lb | ISO 306 | ||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 270 - 300 °C | 518 - 572 °F | |||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat | ||
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | ISO 960 | ||
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | |||
| Descriptive Properties | |||||
| Back Pressure | Low | ||||
| Injection Speed | Fast | ||||