- 吸水率 [%]: 0.6
- 缺口沖擊強度: 3.24
- 彎曲模量 [MPa]: 14.715
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.56 g/cc | 1.56 g/cc | ASTM D792 |
| Water Absorption | 0.60 % @Time 86400 sec | 0.60 % @Time 24.0 hour | |
| Linear Mold Shrinkage | 0.0018 cm/cm | 0.0018 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0022 cm/cm | 0.0022 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 250.155 MPa | 36282.0 psi | ASTM D638 |
| Elongation at Break | 1.9 % | 1.9 % | ASTM D638 |
| Flexural Strength | 362.97 MPa | 52644 psi | ASTM D790 |
| Flexural Modulus | 14.715 GPa | 2134.2 ksi | ASTM D790 |
| Izod Impact, Notched | 3.24 J/cm @Temperature 23.0 °C | 6.06 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| 3.24 J/cm @Temperature -30.0 °C | 6.06 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 249 °C | 480 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 280 - 300 °C | 536 - 572 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |