- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.7
- 缺口沖擊強度: 0.9
- 拉伸強度 [MPa]: 160.0
- 斷裂伸長率 [%]: 270
- 彎曲模量 [MPa]: 7.50
- 熱變形溫度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in3 | ASTM D792 |
| Water Absorption | 0.70 % | 0.70 % | 23°C/24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 160 MPa | 23200 psi | ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Yield Strength | 270 MPa | 39200 psi | ASTM D790 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 252 °C | 486 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |