- 密度 [g/cm3]: 1.1
- 吸水率 [%]: 1.2
- 缺口沖擊強度: 3.0
- 拉伸強度 [MPa]: 67.0
- 斷裂伸長率 [%]: 95.0
- 彎曲模量 [MPa]: 2.30
- 硬度: 112.0
- 熱變形溫度 [℃]: 225.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in3 | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | 23°C/24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 112 | 112 | ASTM D786 |
| Tensile Strength, Yield | 67.0 MPa | 9720 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Yield Strength | 95.0 MPa | 13800 psi | ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790 |
| Izod Impact, Notched | 3.00 J/cm | 5.62 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB @Thickness 3.20 mm | NB @Thickness 0.126 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 75.0 μm/m-°C @Temperature 20.0 °C | 41.7 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Thermal Conductivity | 0.250 W/m-K | 1.74 BTU-in/hr-ft2-°F | |
| Melting Point | 260 °C | 500 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |