- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 2.2
- 拉伸強度 [MPa]: 43.0
- 熱變形溫度 [℃]: 132.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in3 | DAM; ISO 1183 | ||
| Water Absorption | 2.2 % @Temperature 23.0 °C | 2.2 % @Temperature 73.4 °F | DAM; Equilibrium 50%RH; ISO 62, Similar to | ||
| 6.7 % @Temperature 23.0 °C | 6.7 % @Temperature 73.4 °F | DAM; Saturation, immersed; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.017 cm/cm @Thickness 2.00 mm | 0.017 in/in @Thickness 0.0787 in | DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Stress | 39.0 MPa @Strain 50.0 %, Temperature 23.0 °C | 5660 psi @Strain 50.0 %, Temperature 73.4 °F | 50%RH; ISO 527 | ||
| Tensile Strength, Yield | 43.0 MPa @Temperature 23.0 °C | 6240 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 50.0 MPa @Temperature 23.0 °C | 7250 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 32 % @Temperature 23.0 °C | 32 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Elongation at Yield | 5.7 % @Temperature 23.0 °C | 5.7 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 37 % @Temperature 23.0 °C | 37 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 0.900 GPa @Temperature 23.0 °C | 131 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 2.00 GPa @Temperature 23.0 °C | 290 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 50%RH; ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | DAM; ISO 179/1eU | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.70 J/cm2 @Temperature -30.0 °C | 8.09 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 1.80 J/cm2 @Temperature -30.0 °C | 8.57 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 8.00 J/cm2 @Temperature 23.0 °C | 38.1 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 11.5 J/cm2 @Temperature 23.0 °C | 54.7 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 1200 MPa @Temperature 23.0 °C | 174000 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Tensile Creep Modulus, 1000 hours | 750 MPa @Temperature 23.0 °C | 109000 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm @Temperature 23.0 °C | 1.00e+13 ohm-cm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| 1.00e+15 ohm-cm @Temperature 23.0 °C | 1.00e+15 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| Surface Resistance | >= 1.00e+15 ohm @Temperature 23.0 °C | >= 1.00e+15 ohm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| 1.00e+15 ohm @Temperature 23.0 °C | 1.00e+15 ohm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 2.9 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | ||
| 3.2 @Frequency 100 Hz, Temperature 23.0 °C | 3.2 @Frequency 100 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |||
| 3.6 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 3.6 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| 8.0 @Frequency 100 Hz, Temperature 23.0 °C | 8.0 @Frequency 100 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| Dielectric Strength | 31.0 kV/mm @Thickness 1.00 mm, Temperature 23.0 °C | 787 kV/in @Thickness 0.0394 in, Temperature 73.4 °F | DAM; IEC 60243-1 | ||
| 39.0 kV/mm @Thickness 1.00 mm, Temperature 23.0 °C | 991 kV/in @Thickness 0.0394 in, Temperature 73.4 °F | 50%RH; IEC 60243-1 | |||
| Dissipation Factor | 0.0080 @Frequency 100 Hz, Temperature 23.0 °C | 0.0080 @Frequency 100 Hz, Temperature 73.4 °F | DAM; IEC 60250 | ||
| 0.014 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.014 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |||
| 0.055 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.055 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| 0.18 @Frequency 100 Hz, Temperature 23.0 °C | 0.18 @Frequency 100 Hz, Temperature 73.4 °F | 50%RH; IEC 60250 | |||
| Comparative Tracking Index | 600 V @Temperature 23.0 °C | 600 V @Temperature 73.4 °F | DAM; IEC 60112 | ||
| >= 600 V @Temperature 23.0 °C | >= 600 V @Temperature 73.4 °F | DAM; UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 120 μm/m-°C @Temperature 23.0 - 55.0 °C | 66.7 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 120 μm/m-°C @Temperature 23.0 - 55.0 °C | 66.7 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 90.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 50.0 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | ||
| 90.0 μm/m-°C @Temperature 23.0 - 55.0 °C | 50.0 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| Melting Point | 263 °C | 505 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | DAM; ISO 75-1/-2 | ||
| Glass Transition Temp, Tg | 75.0 °C | 167 °F | DAM; 10°C/min; ISO 11357-1/-2 | ||
| UL RTI, Electrical | 125 °C @Thickness 0.810 mm | 257 °F @Thickness 0.0319 in | DAM; UL 746B | ||
| 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 125 °C @Thickness 3.00 mm | 257 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 75.0 °C @Thickness 0.810 mm | 167 °F @Thickness 0.0319 in | DAM; UL 746B | ||
| 75.0 °C @Thickness 1.50 mm | 167 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 75.0 °C @Thickness 3.00 mm | 167 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 85.0 °C @Thickness 0.810 mm | 185 °F @Thickness 0.0319 in | DAM; UL 746B | ||
| 85.0 °C @Thickness 1.50 mm | 185 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 85.0 °C @Thickness 3.00 mm | 185 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 0.810 mm | HB @Thickness 0.0319 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 0.810 mm | HB @Thickness 0.0319 in | DAM; UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| Oxygen Index | 20 % | 20 % | DAM; ISO 4589-1/-2 | ||
| Glow Wire Test | 650 °C @Thickness 3.00 mm | 1200 °F @Thickness 0.118 in | DAM; Flammability Index; IEC 60695-2-12 | ||
| 675 °C @Thickness 0.810 mm | 1250 °F @Thickness 0.0319 in | DAM; Ignition Temp; IEC 60695-2-13 | |||
| 675 °C @Thickness 1.50 mm | 1250 °F @Thickness 0.0591 in | DAM; Ignition Temp; IEC 60695-2-13 | |||
| 675 °C @Thickness 3.00 mm | 1250 °F @Thickness 0.118 in | DAM; Ignition Temp; IEC 60695-2-13 | |||
| 675 °C @Thickness 1.50 mm | 1250 °F @Thickness 0.0591 in | DAM; Flammability Index; IEC 60695-2-12 | |||
| 725 °C @Thickness 0.810 mm | 1340 °F @Thickness 0.0319 in | DAM; Flammability Index; IEC 60695-2-12 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 290 °C | 554 °F | DAM; optimum | ||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; Optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Dehumidified Dryer | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Natural Color | ||||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | ||||
| Forms | Pellets | ||||
| Generic | Nylon 66 | ||||
| Material Status | Current | ||||
| Part Marking Code | >PA66-HI< | ISO 11469 | |||
| Polymer Family | Polyamide | ||||
| Polymer Type | PA66 | ||||
| Processing Method | Injection Molding | ||||
| Product Category | Color Stable Resins | ||||
| Toughened Resins | |||||
| Region Available - Europe | Yes | ||||
| Yes | |||||
| Resin Identification | PA66-HI | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Ultrasonic Weldable | Yes | ||||