- 密度 [g/cm3]: 1.49
- 吸水率 [%]: 2.2
- 缺口沖擊強(qiáng)度: 14.0
- 熱變形溫度 [℃]: 258.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in3 | DAM; ISO 1183 | ||
| Filler Content | 43 % | 43 % | DAM | ||
| Water Absorption | 2.2 % @Thickness 1.00 mm, Temperature 23.0 °C | 2.2 % @Thickness 0.0394 in, Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 7.6 % @Thickness 1.00 mm, Temperature 23.0 °C | 7.6 % @Thickness 0.0394 in, Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 160 MPa @Temperature 23.0 °C | 23200 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 225 MPa @Temperature 23.0 °C | 32600 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 2.5 % @Temperature 23.0 °C | 2.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 3.5 % @Temperature 23.0 °C | 3.5 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 11.0 GPa @Temperature 23.0 °C | 1600 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 14.0 GPa @Temperature 23.0 °C | 2030 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Izod Impact, Notched (ISO) | 14.0 kJ/m2 @Temperature 23.0 °C | 6.66 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | ||
| 16.0 kJ/m2 @Temperature 23.0 °C | 7.61 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 9.00 J/cm2 @Temperature 23.0 °C | 42.8 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| 9.50 J/cm2 @Temperature 23.0 °C | 45.2 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 1.60 J/cm2 @Temperature 23.0 °C | 7.61 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| 1.80 J/cm2 @Temperature 23.0 °C | 8.57 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm @Temperature 23.0 °C | 1.00e+16 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | ||
| Dissipation Factor | 0.013 @Frequency 100 Hz, Temperature 23.0 °C | 0.013 @Frequency 100 Hz, Temperature 73.4 °F | DAM; IEC 60250 | ||
| 0.015 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.015 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | DAM; IEC 60250 | |||
| Comparative Tracking Index | 600 V @Temperature 23.0 °C | 600 V @Temperature 73.4 °F | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 258 °C | 496 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | DAM; ISO 75-1/-2 | ||
| Glass Transition Temp, Tg | 80.0 °C | 176 °F | 10°C/min; DAM; ISO 11357-1/-2 | ||
| Oxygen Index | 24 % | 24 % | DAM; ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 295 °C | 563 °F | DAM; Optimum | |||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Heat Stabilizer | DAM | |||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Chemical Resistance, Good | DAM | |||
| Creep Resistance, Good | DAM | ||||
| Fatigue Resistant | DAM | ||||
| Fuel Resistant | DAM | ||||
| Grease Resistant | DAM | ||||
| Heat Aging Resistance, Good | DAM | ||||
| Heat Stabilized | DAM | ||||
| Oil Resistant | DAM | ||||
| Stiffness, High | DAM | ||||
| Strength, High | DAM | ||||
| Thermal Aging Resistance, Good | DAM | ||||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-GF43< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66-GF43 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Uses | Appliance Components | DAM | |||
| Automotive Applications | DAM | ||||
| Electrical/Electronic Applications | DAM | ||||
| Industrial Applications | DAM | ||||