- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 2.1
- 缺口沖擊強度: 0.64
- 彎曲模量 [MPa]: 3.72
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in3 | DAM; ISO 1183 | ||
| Filler Content | 15 % | 15 % | DAM | ||
| Water Absorption | 2.1 % @Temperature 23.0 °C | 2.1 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 7.7 % @Temperature 23.0 °C | 7.7 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.011 cm/cm @Thickness 2.00 mm | 0.011 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Thickness 2.00 mm | 0.011 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 52.0 MPa @Temperature 23.0 °C | 7540 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 76.0 MPa @Temperature 23.0 °C | 11000 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Strength | 79.0 MPa @Temperature 23.0 °C | 11500 psi @Temperature 73.4 °F | DAM; ASTM D638 | ||
| Elongation at Break | 17 % @Temperature 23.0 °C | 17 % @Temperature 73.4 °F | DAM; ASTM D638 | ||
| 21 % @Temperature 23.0 °C | 21 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| 52 % @Temperature 23.0 °C | 52 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 1.80 GPa @Temperature 23.0 °C | 261 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 3.80 GPa @Temperature 23.0 °C | 551 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 3.72 GPa @Temperature 23.0 °C | 540 ksi @Temperature 73.4 °F | DAM; ASTM D790 | ||
| Izod Impact, Notched | 0.640 J/cm @Temperature 23.0 °C | 1.20 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 @Temperature 23.0 °C | 2.86 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | ||
| 11.0 kJ/m2 @Temperature 23.0 °C | 5.23 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Charpy Impact Unnotched | 0.600 J/cm2 @Temperature -30.0 °C | 2.86 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eU | ||
| 10.0 J/cm2 @Temperature 23.0 °C | 47.6 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.750 J/cm2 @Temperature 23.0 °C | 3.57 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| 1.50 J/cm2 @Temperature 23.0 °C | 7.14 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 295 °C | 563 °F | DAM; Optimum | |||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Filler | Mineral filler | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Heat Stabilized | Yes | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-IMD15< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Low Warp Resins | DAM | |||
| Mineral Reinforced Resins | DAM | ||||
| Resin Identification | PA66-IMD15 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||