- 缺口沖擊強(qiáng)度: 1.6
- 拉伸強(qiáng)度 [MPa]: 60.0
- 彎曲模量 [MPa]: 1.795
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.012 cm/cm @Thickness 3.17 mm | 0.012 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Modulus | 1.795 GPa | 260.3 ksi | ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 3.00 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 252 °C | 486 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |